This is an old revision of the document!
Table of Contents
The window
The Plan
My initial plan for the window is:
- Cut a few circles out of some float glass,
- Clean them thoroughly with IPA and HCL,
- Build a stack of them to the desired thickness,
- Fire in kiln:
- Slow ramp to 775°C,
- Hold for five minutes,
- Fast ramp down to 565°C,
- Hold for 10 min,
- Slow ramp down to room temperature.
- Polish,
- Harden in a 400°C bath of potassium nitrate.
I had good success tempering bottle glass with a 560°C soak in the glass sphere project. This superb reference suggests that 565°C is a good tempering temperature for float glass, and 775°C is a good fusing temperature.
The Doing
Cutting out circles of glass.
Stack of circles. There are some cracks, but they'll reform during the firing.
Soaking the circles in 320G/L HCL acid.
Programming up the curve in my furnace. I don't understand this software very well.
Stacked up, ready for firing.
Some of the glass broke during the warm-up, and spat part of a circle out of the stack. I was able to nudge it back into position with a metal rod. I think a slower warm-up ramp would be a good idea.
After firing.