Line 6: | Line 6: | ||
===== The Plan ===== | ===== The Plan ===== | ||
- | I wanted to run a medium-duration test of the electrically-complete blinker before going through all the trouble and expense of encasing it in aluminium and glass. I decided to cast the electronics in transparent resin. This would be reasonably mechanically and chemically robust, but it would degrade in sunlight over a few years, turning yellow and crumbling. | + | I wanted to run a medium-duration test of the electrically-complete blinker before going through all the trouble and expense of encasing it in aluminium and glass. I decided to cast the electronics in transparent resin. This would be reasonably mechanically and chemically robust, but it would degrade in sunlight over a few years, turning yellow and crumbling. |
===== The Results ===== | ===== The Results ===== | ||
Line 25: | Line 25: | ||
Not too bad! | Not too bad! | ||
- | I was reasonably happy with this result. There is some white discolouration on the solar cells visible in that photo. That discolouration wasn't present when I took the panel out of the mould. It formed shortly after I put it in the sun for this test. It seems to have been formed by some combination of: | + | I was reasonably happy with this result. There is some grey discolouration on the solar cells visible in that photo. That discolouration wasn't present when I took the panel out of the mould. It formed shortly after I put it in the sun for this test. It seems to have been formed by some combination of: |
* UV radiation, | * UV radiation, |