Differences

This shows you the differences between two versions of the page.

--- projects:blinker:work_logs:2_window [2022/01/23 11:17] – [The Doing] tjhowse
+++ projects:blinker:work_logs:2_window [2022/01/31 03:52] – tjhowse
@@ Line 8: / Line 8: @@
   * Cut a few circles out of some float glass,
   * Clean them thoroughly with IPA and HCL,
-  * Build a stack of them in the kiln of the desired thickness,
+  * Build a stack of them to the desired thickness,
-  * Fire:
+  * Fire in kiln:
     * Slow ramp to 775°C,
     * Hold for five minutes,
@@ Line 34: / Line 34: @@
 Soaking the circles in 320G/L HCL acid.
-{{:projects:blinker:work_logs:pasted:20220123-054505.png}}
+{{:projects:blinker:work_logs:pasted:20220124-073400.png}}
-Programming up the curve in my furnace.
+Programming up the curve in my furnace. I don't understand this software very well.
 {{:projects:blinker:work_logs:pasted:20220123-111739.png}}
 Stacked up, ready for firing.
+{{:projects:blinker:work_logs:pasted:20220124-035844.png}}
+Some of the glass broke during the warm-up, and spat part of a circle out of the stack. I was able to nudge it back into position with a metal rod. I think a slower warm-up ramp would be a good idea.
+{{:projects:blinker:work_logs:pasted:20220124-100459.png}}
+After firing. Clarity is good. I can see some air trapped between the layers, and some other general gunk stuck in there. I think I need to use distilled water to wash after the acid bath. The cracks did not fully amalgamate, and I suspect some of the layers did not properly bond together. I might try increasing the max temperature. I have done a few experimental drops and general rough handling and it shows no sign of damage. I haven't been brave enough to drop it onto concrete or anything.
+{{:projects:blinker:work_logs:pasted:20220125-034206.png}}
+Second firing profile.
+{{:projects:blinker:work_logs:pasted:20220126-050746.png}}
+{{:projects:blinker:work_logs:pasted:20220126-050802.png}}
+{{:projects:blinker:work_logs:pasted:20220126-050817.png}}
+After the second firing. It definitely appears to have merged together more thoroughly. Some of the fine internal cracks have become invisible. I'm not sure whether this is because of the higher peak temperature or the longer time spend at temperature.
+{{:projects:blinker:work_logs:pasted:20220131-035238.png}}
+Re-firing window 1, firing window 2 for the first time.
+{{:projects:blinker:work_logs:pasted:20220131-035156.png}}
+A slower initial ramp, this time,
  [<6>]